BS EN ISO 14574:2016
$142.49
Fine ceramics (advanced ceramics, advanced technical ceramics). Mechanical properties of ceramic composites at high temperature. Determination of tensile properties
| Published By | Publication Date | Number of Pages |
| BSI | 2016 | 26 |
This International Standard specifies the conditions for determination of tensile properties of ceramic matrix composite materials with continuous fibre reinforcement for temperatures up to 2 000 °C.
In most cases, ceramic matrix composites to be used at high temperature in air are coated with an antioxidation coating.
The purpose of this International Standard is to determine the tensile properties of a material when it is placed under an oxidizing environment but not to measure material oxidation.
This International Standard applies to all ceramic matrix composites with a continuous fibre reinforcement, unidirectional (1D), bi-directional (2D), and tri-directional ( xD, with 2 < x ≤ 3), loaded along one principal axis of reinforcement.
PDF Catalog
| PDF Pages | PDF Title |
|---|---|
| 4 | European foreword |
| 6 | Foreword |
| 7 | Section sec_1 Section sec_2 Section sec_3 1 Scope 2 Normative references 3 Terms, definitions and symbols |
| 10 | Section sec_4 Section sec_5 Section sec_5.1 Section sec_5.2 Section sec_5.3 4 Principle 5 Apparatus 5.1 Test machine 5.2 Load train 5.3 Test chamber |
| 11 | Section sec_5.4 Section sec_5.5 Section sec_5.6 Section sec_5.7 5.4 Set-up for heating 5.5 Extensometer 5.6 Temperature measurement devices 5.7 Data recording system |
| 12 | Section sec_5.8 Section sec_6 Section sec_6.1 Section sec_6.2 Figure fig_1 5.8 Micrometers 6 Test specimens 6.1 General 6.2 Test specimens commonly used |
| 13 | Table tab_1 Figure fig_2 Table tab_2 |
| 14 | Figure fig_3 Table tab_3 Figure fig_4 |
| 15 | Table tab_4 Figure fig_5 Table tab_5 |
| 16 | Figure fig_6 Table tab_6 Section sec_7 Section sec_7.1 Section sec_7.2 7 Test specimen preparation 7.1 Machining and preparation 7.2 Number of tests of specimens |
| 17 | Section sec_8 Section sec_8.1 Section sec_8.1.1 Section sec_8.1.2 Section sec_8.1.3 Section sec_8.2 Section sec_8.2.1 Section sec_8.2.2 8 Test procedures 8.1 Test set-up: Temperature considerations 8.2 Test set-up: Other considerations |
| 18 | Section sec_8.3 Section sec_8.3.1 Section sec_8.3.2 Section sec_8.3.3 Section sec_8.3.4 Section sec_8.3.5 8.3 Testing technique |
| 19 | Section sec_8.4 Section sec_9 Section sec_9.1 Section sec_9.2 Section sec_9.3 8.4 Test validity 9 Calculation of results 9.1 Test specimen origin 9.2 Tensile strength 9.3 Strain at maximum tensile force |
| 20 | Section sec_9.4 Section sec_9.4.1 Section sec_9.4.2 9.4 Proportionality ratio or Pseudo-elastic modulus, elastic modulus |
| 21 | Section sec_9.4.3 Section sec_10 10 Test report |
| 22 | Annex sec_A Table tab_e Figure fig_A.1 Annex A (informative) Test specimen for use with optical extensometry |
| 23 | Reference ref_1 Reference ref_2 Bibliography |